片状石墨奥氏体铸铁的牌号与化学成分（质量分数）（%）
|
牌 号 |
C |
Si |
Mn |
Cr |
Ni |
Cu |
|
L-NiMn137 |
≤3.0 |
1.5~3.0 |
6.0~7.0 |
≤0.2 |
12.0~14.0 |
≤0.5 |
|
L-NiCuCr1562 |
≤3.0 |
1.0~2.8 |
0.5~1.5 |
1.0~2.5 |
13.5~17.5 |
5.5~7.5 |
|
L-NiCuCr1563 |
≤3.0 |
1.0~2.8 |
0.5~1.5 |
2.5~3.5 |
13.5~17.5 |
5.5~7.5 |
|
L-NiCr202 |
≤3.0 |
1.0~2.8 |
0.5~1.5 |
1.0~2.5 |
18.0~22.0 |
≤0.5 |
|
L-NiCr203 |
≤3.0 |
1.0~2.8 |
0.5~1.5 |
2.5~3.5 |
18.0~22.0 |
≤0.5 |
|
L-NiSiCr2053 |
≤2.5 |
4.5~5.5 |
0.5~1.5 |
1.5~4.5 |
18.0~22.0 |
≤0.5 |
|
L-NiCr303 |
≤2.5 |
1.0~2.0 |
0.5~1.5 |
2.5~3.5 |
28.0~32.0 |
≤0.5 |
|
L-NiCr3055 |
≤2.5 |
5.0~6.0 |
0.5~1.5 |
4.5~5.5 |
28.0~32.0 |
≤0.5 |
|
L-Ni35 |
≤2.4 |
1.0~2.0 |
0.5~1.5 |
≤0.2 |
34.0~36.0 |
≤0.5 |
片状石墨奥氏体铸铁的力学能力
|
牌 号 |
抗拉强度
σb≥/MPa |
抗压强度
σbc≥/MPa |
伸长率
δ≥（%） |
弹性模量
G/GPa |
硬度
HBS |
|
L-NiMn137 |
140~220 |
630~840 |
－ |
70~90 |
120~150 |
|
L-NiCuCr1562 |
170~210 |
700~840 |
２ |
85~105 |
140~200 |
|
L-NiCuCr1563 |
190~240 |
860~1100 |
1~2 |
98~113 |
150~250 |
|
L-NiCr202 |
170~210 |
700~840 |
2~3 |
85~105 |
120~215 |
|
L-NiCr203 |
190~240 |
860~2200 |
1~2 |
98~113 |
160~250 |
|
L-NiSiCr2053 |
190~280 |
860~1100 |
2~3 |
110 |
140~250 |
|
L-NiCr303 |
190~240 |
700~910 |
1~3 |
98~113 |
120~215 |
|
L-NiCr3055 |
170~240 |
≥560 |
－ |
105 |
150~210 |
|
L-Ni35 |
120~180 |
560~700 |
1~3 |
74 |
120~140 |
球状石墨奥氏体铸铁的牌号与化学成分（质量分数）（%）
|
牌 号 |
C |
Si |
Mn |
Cr |
Ni |
P
≤ |
Cu
≤ |
|
S-NiMn137 |
≤3.0 |
2.0~3.0 |
6.0~7.0 |
≤0.2 |
12.0~14.0 |
0.080 |
0.5 |
|
S-NiCr202 |
≤3.0 |
1.5~3.0 |
0.5~1.5 |
1.0~2.5 |
18.0~22.0 |
0.080 |
0.5 |
|
S-NiCr203 |
≤3.0 |
1.5~3.0 |
0.5~1.5 |
2.5~3.5 |
18.0~22.0 |
0.080 |
0.5 |
|
S-NiSiCr2052 |
≤3.0 |
4.5~5.5 |
0.5~1.5 |
1.0~2.5 |
18.0~22.0 |
0.080 |
0.5 |
|
S-Ni22 |
≤3.0 |
1.0~3.0 |
1.5~2.5 |
≤0.5 |
21.0~24.0 |
0.080 |
0.5 |
|
S-NiMn234 |
≤2.6 |
1.5~2.5 |
4.0~4.5 |
≤0.2 |
22.0~24.0 |
0.080 |
0.5 |
|
S-NiCr301 |
≤2.6 |
1.5~3.0 |
0.5~1.5 |
1.0~1.5 |
28.0~32.0 |
0.080 |
0.5 |
|
S-NiCr303 |
≤2.6 |
1.5~3.0 |
0.5~1.5 |
2.5~3.5 |
28.0~32.0 |
0.080 |
0.5 |
|
S-NiSiCr3055 |
≤2.6 |
5.0~6.0 |
0.5~1.5 |
4.5~5.5 |
28.0~32.0 |
0.080 |
0.5 |
|
S-Ni35 |
≤2.4 |
1.5~3.0 |
0.5~1.5 |
≤0.2 |
34.0~36.0 |
0.080 |
0.5 |
|
S-NiCr353 |
≤2.4 |
1.5~3.0 |
0.5~1.5 |
2.0~3.0 |
34.0~36.0 |
0.080 |
0.5 |
|
牌 号 |
C抗拉强度
σb≥/MPa |
屈服强度
σ0.2≥/Mpa |
伸长率
δ≥（%） |
弹性模量
G/Mpa×103 |
冲击吸收功
AKV/J |
硬度
HBS |
|
S-NiMn137 |
390~460 |
210~260 |
15~25 |
140~150 |
15.0~27.5 |
130~170 |
|
S-NiCr202 |
370~470 |
210~250 |
7~20 |
112~130 |
13.5~27.5 |
140~200 |
|
S-NiCr203 |
390~490 |
210~260 |
7~15 |
112~133 |
12.0 |
150~255 |
|
0S-NiSiCr2052 |
370~430 |
210~260 |
10~18 |
112~133 |
14.9 |
180~230 |
|
S-Ni22 |
370~440 |
170~250 |
20~40 |
85~112 |
20.0~33.00 |
130~170 |
|
S-NiMn234 |
440~470 |
210~240 |
25~45 |
120~140 |
24.0 |
150~180 |
|
S-NiCr301 |
370~440 |
210~270 |
13~18 |
112~130 |
17.0 |
130~190 |
|
S-NiCr303 |
370~470 |
210~260 |
7~18 |
92~105 |
8.5 |
140~200 |
|
S-NiSiCr3055 |
390~490 |
240~310 |
1~4 |
91 |
3.9~5.9 |
170~250 |
|
S-Ni35 |
370~410 |
210~240 |
20~40 |
112~140 |
20.5 |
130~180 |
|
S-NiCr353 |
370~440 |
210~290 |
7~10 |
112~123 |
7.0 |
140~180 |